Sintering behavior and alloying elements effects on the properties of CP-Titanium sintered using pulsed electric current

Samson Olaitan Jeje, Mxolisi Brendon Shongwe, Nthabiseng Maledi, Enoch Nifise Ogunmuyiwa, Lerato Criselda Tshabalala, Bukola Joseph Babalola, Peter Apata Olubambi

Research output: Contribution to journalArticle

Abstract

Mechanical properties of grade 1 commercially pure titanium (CP–Ti) are characterized by a good combination of strength and ductility at elevated temperatures. CP-Ti mechanical properties at room and elevated temperature can be enhanced by alloying with other elements to meet up with its demand for industrial applications. In this study, the effect of Al–Mo addition and sintering temperature on the densification, microstructure, and mechanical properties of spark plasma sintered CP-Ti compacts were investigated. CP-Ti and Ti–7Al–1Mo (wt.%) compacts sintering were carried out at a constant holding time of 10 min, pressure of 50 MPa and sintering temperature of 800 °C, 1000 °C, and 1100 °C under vacuum. Full densification with Vickers hardness values of 352 ± 17 H V was obtained for the developed Ti–7Al–1Mo alloy at 1000 °C. Different microstructural transformations and phase evolution were observed in the as-sintered compact with respect to sintering temperature. The role of the alloying element and sintering temperature on the relative density, microstructure, hardness, and wear of the as-sintered samples were discussed. This paper shows that alloying of CP-Ti with Al and Mo enhances its microstructure and mechanical properties.

Original languageEnglish
Article number123707
JournalMaterials Chemistry and Physics
Volume256
DOIs
Publication statusPublished - Dec 1 2020

All Science Journal Classification (ASJC) codes

  • Materials Science(all)
  • Condensed Matter Physics

Fingerprint Dive into the research topics of 'Sintering behavior and alloying elements effects on the properties of CP-Titanium sintered using pulsed electric current'. Together they form a unique fingerprint.

  • Cite this