Corrosion cracking of a mild steel in orange juice

Ayo S. Afolabi, Tinyiko G. Ngwenya, Kazeem O. Sanusi, Ambali S. Abdulkareem

Research output: Chapter in Book/Report/Conference proceedingConference contribution

Abstract

Stress corrosion cracking (SCC) results from the combined action of three factors: The tensile stresses in the material, a corrosive medium and elevated temperature. In this study, the stress corrosion cracking and microstructural analysis of a mild steel immersed in orange juice medium was investigated using weight loss technique and SEM analysis. The mild steel coupons were heat treated to various austenitic temperatures, cooled in water and immersed in orange juice. The weight losses of the mild steel samples were measured at a two days interval and the corrosion rate was the determined. The results obtained show that SCC relative to mild steel is mainly a function of the acidity of the medium under study, and the corrosion rate increases with increase in exposure time throughout the exposure time. Also, the higher the austenitic temperature the more the resistance to corrosion attack due to higher hardness obtained at higher temperatures. The SEM analysis revealed that the transgranular and intergranular attacks were visibly responsible for the corrosion of this material in this medium. The evolution of hydrogen at low pH of the medium due to the presence of acidic citric acid eliminated the possibility of protective formation on the throughout the exposure period.

Original languageEnglish
Title of host publicationProceedings of the World Congress on Engineering 2013, WCE 2013
Pages512-515
Number of pages4
Volume1 LNECS
Publication statusPublished - Nov 25 2013
Event2013 World Congress on Engineering, WCE 2013 - London, United Kingdom
Duration: Jul 3 2013Jul 5 2013

Other

Other2013 World Congress on Engineering, WCE 2013
CountryUnited Kingdom
CityLondon
Period7/3/137/5/13

Fingerprint

Stress corrosion cracking
Carbon steel
Corrosion rate
Corrosion
Temperature
Scanning electron microscopy
Citric acid
Acidity
Tensile stress
Hardness
Hydrogen
Water

All Science Journal Classification (ASJC) codes

  • Computer Science (miscellaneous)

Cite this

Afolabi, A. S., Ngwenya, T. G., Sanusi, K. O., & Abdulkareem, A. S. (2013). Corrosion cracking of a mild steel in orange juice. In Proceedings of the World Congress on Engineering 2013, WCE 2013 (Vol. 1 LNECS, pp. 512-515)
Afolabi, Ayo S. ; Ngwenya, Tinyiko G. ; Sanusi, Kazeem O. ; Abdulkareem, Ambali S. / Corrosion cracking of a mild steel in orange juice. Proceedings of the World Congress on Engineering 2013, WCE 2013. Vol. 1 LNECS 2013. pp. 512-515
@inproceedings{34b8b91d709849cca901fa7cda33075e,
title = "Corrosion cracking of a mild steel in orange juice",
abstract = "Stress corrosion cracking (SCC) results from the combined action of three factors: The tensile stresses in the material, a corrosive medium and elevated temperature. In this study, the stress corrosion cracking and microstructural analysis of a mild steel immersed in orange juice medium was investigated using weight loss technique and SEM analysis. The mild steel coupons were heat treated to various austenitic temperatures, cooled in water and immersed in orange juice. The weight losses of the mild steel samples were measured at a two days interval and the corrosion rate was the determined. The results obtained show that SCC relative to mild steel is mainly a function of the acidity of the medium under study, and the corrosion rate increases with increase in exposure time throughout the exposure time. Also, the higher the austenitic temperature the more the resistance to corrosion attack due to higher hardness obtained at higher temperatures. The SEM analysis revealed that the transgranular and intergranular attacks were visibly responsible for the corrosion of this material in this medium. The evolution of hydrogen at low pH of the medium due to the presence of acidic citric acid eliminated the possibility of protective formation on the throughout the exposure period.",
author = "Afolabi, {Ayo S.} and Ngwenya, {Tinyiko G.} and Sanusi, {Kazeem O.} and Abdulkareem, {Ambali S.}",
year = "2013",
month = "11",
day = "25",
language = "English",
isbn = "9789881925107",
volume = "1 LNECS",
pages = "512--515",
booktitle = "Proceedings of the World Congress on Engineering 2013, WCE 2013",

}

Afolabi, AS, Ngwenya, TG, Sanusi, KO & Abdulkareem, AS 2013, Corrosion cracking of a mild steel in orange juice. in Proceedings of the World Congress on Engineering 2013, WCE 2013. vol. 1 LNECS, pp. 512-515, 2013 World Congress on Engineering, WCE 2013, London, United Kingdom, 7/3/13.

Corrosion cracking of a mild steel in orange juice. / Afolabi, Ayo S.; Ngwenya, Tinyiko G.; Sanusi, Kazeem O.; Abdulkareem, Ambali S.

Proceedings of the World Congress on Engineering 2013, WCE 2013. Vol. 1 LNECS 2013. p. 512-515.

Research output: Chapter in Book/Report/Conference proceedingConference contribution

TY - GEN

T1 - Corrosion cracking of a mild steel in orange juice

AU - Afolabi, Ayo S.

AU - Ngwenya, Tinyiko G.

AU - Sanusi, Kazeem O.

AU - Abdulkareem, Ambali S.

PY - 2013/11/25

Y1 - 2013/11/25

N2 - Stress corrosion cracking (SCC) results from the combined action of three factors: The tensile stresses in the material, a corrosive medium and elevated temperature. In this study, the stress corrosion cracking and microstructural analysis of a mild steel immersed in orange juice medium was investigated using weight loss technique and SEM analysis. The mild steel coupons were heat treated to various austenitic temperatures, cooled in water and immersed in orange juice. The weight losses of the mild steel samples were measured at a two days interval and the corrosion rate was the determined. The results obtained show that SCC relative to mild steel is mainly a function of the acidity of the medium under study, and the corrosion rate increases with increase in exposure time throughout the exposure time. Also, the higher the austenitic temperature the more the resistance to corrosion attack due to higher hardness obtained at higher temperatures. The SEM analysis revealed that the transgranular and intergranular attacks were visibly responsible for the corrosion of this material in this medium. The evolution of hydrogen at low pH of the medium due to the presence of acidic citric acid eliminated the possibility of protective formation on the throughout the exposure period.

AB - Stress corrosion cracking (SCC) results from the combined action of three factors: The tensile stresses in the material, a corrosive medium and elevated temperature. In this study, the stress corrosion cracking and microstructural analysis of a mild steel immersed in orange juice medium was investigated using weight loss technique and SEM analysis. The mild steel coupons were heat treated to various austenitic temperatures, cooled in water and immersed in orange juice. The weight losses of the mild steel samples were measured at a two days interval and the corrosion rate was the determined. The results obtained show that SCC relative to mild steel is mainly a function of the acidity of the medium under study, and the corrosion rate increases with increase in exposure time throughout the exposure time. Also, the higher the austenitic temperature the more the resistance to corrosion attack due to higher hardness obtained at higher temperatures. The SEM analysis revealed that the transgranular and intergranular attacks were visibly responsible for the corrosion of this material in this medium. The evolution of hydrogen at low pH of the medium due to the presence of acidic citric acid eliminated the possibility of protective formation on the throughout the exposure period.

UR - http://www.scopus.com/inward/record.url?scp=84887860219&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=84887860219&partnerID=8YFLogxK

M3 - Conference contribution

SN - 9789881925107

VL - 1 LNECS

SP - 512

EP - 515

BT - Proceedings of the World Congress on Engineering 2013, WCE 2013

ER -

Afolabi AS, Ngwenya TG, Sanusi KO, Abdulkareem AS. Corrosion cracking of a mild steel in orange juice. In Proceedings of the World Congress on Engineering 2013, WCE 2013. Vol. 1 LNECS. 2013. p. 512-515